| 建議零售價 | ,？,？0.00 |
|---|---|
| 廠家(產(chǎn)地) | 日本東麗 |
| 牌號 | CM3004G-15 |
| 加工級別 | 注塑級 |
| 特性級別 | 增強級,阻燃級 |
| 用途級別 | 纖維 |
| 銷售方式 | 品牌經(jīng)銷 |
| 類型 | 標(biāo)準(zhǔn)料 |
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |||
| 基本性能 | 吸水率 | 23℃,，24小時 | ASTM D-570 |
| % | ||
| 物理性能 | 比重 | ASTM D-792 |
| ||||
| 機械性能 | 斷裂伸長率 | 23℃ | ASTM D-638 |
| % | ||
| 撓曲強度 | 23℃ | ASTM D-790 |
| Kg/cm2 | |||
| 撓曲模量 | 23℃ | ASTM D-790 |
| Kg/cm2 | |||
| 抗拉斷裂強度 | 23℃ | ASTM D-638 |
| Kg/cm2 | |||
| IZOD沖擊強度 | 23℃，無缺口1/8 |
| kg·cm/cm2 | ||||
| 電氣性能 | 體積電阻率 | ASTM D-257 |
| Ω.cm | |||
| 介電常數(shù) | 106Hz | ASTM D-150 |
| ||||
| 損耗因數(shù) | 106Hz | ASTM D-150 |
| ||||
| 抗電弧性 | 1/8" | ASTM D-495 |
| s | |||
| 介電強度 | 1/8" | ASTM D-149 |
| KV/mm | |||
| IEC導(dǎo)電徑跡指數(shù) | UL 746 |
| V | ||||
| 熱性能 | 熱撓曲溫度 | 18.6kg/cm2 | ASTM D-648 |
| ℃ | ||
| 熔點 | 差示掃描測熱計DSC |
| ℃ | ||||
| 線性熱膨脹系數(shù) | ASTM D-696 |
| ×10-5cm/cm/℃ | ||||
| UL-94抗燃級 | UL 94 |
| |||||
| 其它性能 | 強化含量 |
| WT% | ||||
產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 物理性能 | 填充含量 | 15 | Wt% | |||
| 比重 | D792 | 1.47 | ||||
| 吸水率 | - | 23℃,24hrs | D570 | 0.4 | % | |
| - | 23℃,水中 | D570 | 5.0 | % | ||
| 洛氏硬度 | 23℃ | D785 | 120 | R | ||
| 機械性能 | 拉伸屈服強度 | - | -40℃ | D638 | 145 | MPa |
| - | 23℃ | D638 | 125 | MPa | ||
| - | 80℃ | D638 | 60 | MPa | ||
| 斷裂伸長率 | - | 23℃ | D638 | 5 | % | |
| 彎曲強度 | - | 23℃ | D790 | 190 | MPa | |
| - | 80℃ | D790 | 120 | MPa | ||
| 彎曲模量 | - | 23℃ | D790 | 5.7 | Gpa | |
| - | 80℃ | D790 | 3.2 | Gpa | ||
| 沖擊強度 | - | 23℃ | D256 | 40 | J/M | |
| - | 23℃ | D256 | 50 | KJ/m2 | ||
| 磨耗 | D1044 | 12 | mg/1000 | |||
| 電氣性能 | 體積電阻率 | D257 | 1013 | Ω.m | ||
| 加工性能 | 縮模率 | - | 1mmt | 0.4-0.6 | % | |
| - | 3mmt | 0.8-1.2 | % | |||
| 熱性能 | 熔點 | DSC | 265 | ℃ | ||
| 熱變形溫度 | 1.86MPa | D648 | 244 | ℃ | ||
| 阻燃性 | UL94 | V-0 | ||||