| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 霧度2 | 40 mil | ASTM D-1003 | 88@50mils | % |
| 密度 | ExxonMobil Method | 0.902 | g/cm3 | ||
| 熔融指數(shù) | ASTM D-1238 | 3.0 | g/10 min | ||
| 硬度2 | Shore A,15 sec | ASTM D-2240 | 87 | ||
| 熔體流動速率 | ASTM D-1238 | 6.8 | g/10 min | ||
| 硬度2 | Shore D,15 sec | ASTM D-2240 | 42 | ||
| 物理性能 | 拉伸率 | @Break | ASTM D-638 | No Break | % |
| 沖擊強度 | 23℃ | ASTM D-256 | No Break | ft-lb/in(J/m) | |
| 拉伸強度3 | @Break | ASTM D-638 | No Break | psi(MPa) | |
| 沖擊強度 | -40℃ | ASTM D-256 | No Break | ft-lb/in(J/m) | |
| 彎曲模量 | 1% secant | ASTM D-790 | 11,，100（76.5） | psi(MPa) | |
| 熱性能 | 最高熔體溫度 | ExxonMobil Method | 201.4(94.1) | ℉(℃) | |
| 維卡軟化點2 | 200g | ASTM D-1525 | 200.3(93.5) | ℉(℃) | |
| 其它性能 | 拉伸應力5 | @100% Elongation | ASTM D-412 | 943（6.5） | psi(MPa) |
| 拉伸率 | @Break | ASTM D-412 | No Break | % | |
| 抗扯強度 | ASTM D-624 | 428.7(75.1) | lb/in(kN/m) | ||
| 門尼粘度ML(1+4) | 125℃ | ASTM D-1646 | 9.1 | Torgue Units | |
| 抗拉強度 | @Peak | ASTM D-412 | No Break | psi(MPa) | |
| 拉伸應力5 | @300% Elongation | ASTM D-412 | 986(6.8) | psi(MPa) | |