| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 密度 | --- | ASTM D-792(GB 1033) | 1.18 | g/cm3 |
| 熔體流動(dòng)速率 | --- | --- | 15 | g/10min | |
| 物理性能 | 阻燃性 | 3.2mm | UL 94 | HB | --- |
| 阻燃性 | 1.6mm | UL 94 | HB | --- | |
| 機(jī)械性能 | 拉伸強(qiáng)度 | --- | ASTM D-638(GB 1040) | 38 | MPa |
| 伸長(zhǎng)率 | --- | --- | 15 | % | |
| 彎曲強(qiáng)度 | --- | ASTM D-790(GB 9341) | 62 | MPa | |
| 彎曲模量 | --- | ASTM D-790(GB 9341) | 2370 | MPa | |
| 缺口沖擊強(qiáng)度 | --- | ASTM D-256 | 12 | KJ/m2 | |
| 非缺口沖擊強(qiáng)度 | --- | GB 1043 | 不斷 | KJ/m2 | |
| 硬度 | --- | --- | 99.2 | --- | |
| 加工性能 | 成型收縮率 | --- | ASTM D-955(GB 15585) | 0.4-0.6 | % |
| 熱 性 能 | 熱變形溫度 | --- | ASTM D-648(GB 1634) | 95.2 | ℃ |
| 維卡軟化點(diǎn) | --- | --- | 101.1 | ℃ | |