產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 吸水量 | 浸泡均衡點(diǎn)+73℉(+23℃) | ASTM D570 | 0.90 | % |
| 吸水量 | Equil.50%R.h.+73℉(+23℃) | ASTM D570 | 0.22 | % | |
| 密度 | ASTM D792 | 1.42 | |||
| 吸水量 | 24hrs浸泡+73℉(+23℃) | ASTM D570 | 0.25 | % | |
| 物理性能 | 絕緣強(qiáng)度 | Short Time,90 mils | ASTM D149 | 500 | V/mil |
| 絕緣系數(shù) | 系數(shù) +73℉(+23℃)102to106Hz | ASTM D150 | 3.7 | ||
| 絕緣強(qiáng)度 | Short Time,2.3mm | ASTM D149 | 19.7 | MV/m | |
| 擴(kuò)散因數(shù) | +73℉(+23℃)106Hz | ASTM D150 | 0.005 | ||
| 摩擦系數(shù) | +73℉(+23℃)靜態(tài) | 0.20 | ThrustWasherTest3 | ||
| 摩擦系數(shù) | +73℉(+23℃)動態(tài) | ThrustWasherTest3 | 0.35 | ||
| 電阻系數(shù) | +73°F(+23℃)0.2%H2O | ASTM D257 | 1015 | ohm-cm | |
| 機(jī)械性能 | 伸張強(qiáng)度 | +122℃ | ASTM D638 | 26.2 | MPa |
| 撓曲系數(shù) | +212℉ | 在25℃下 | 130 | MPsi | |
| 彎曲降服強(qiáng) | +23℃ | ASTM D790 | 98.6 | MPa | |
| 撓曲系數(shù) | +122℃ | 在25℃下 | 620 | MPa | |
| 伸張強(qiáng)度 | +212℉ | ASTM D638 | 5.2 | Mpsi | |
| lzod沖擊強(qiáng)度 | +23℃ | ASTM D256 | 123 | j/m | |
| 洛氏硬度 | ASTM D785 | M94,R120 | |||
| 斷裂時之拉力伸張度 | +158℉(+70℃) | ASTM D638 | 230 | % | |
| 伸張強(qiáng)度 | -55℃ | ASTM D638 | 101 | MPa | |
| 撓曲系數(shù) | -68℉ | 在25℃下 | 530 | MPsi | |
| 撓曲系數(shù) | -55℃ | 在25℃下 | 3650 | MPa | |
| 無切口沖擊程度 | +23℃ | D256 | >5300(no break) | j/m | |
| 撓曲系數(shù) | +70℃ | 在25℃下 | 1550 | MPa | |
| 撓曲系數(shù) | +250℉ | 在25℃下 | 90 | MPsi | |
| 壓縮應(yīng)力 | 縮應(yīng)力 +73°F@1%Def. | ASTM D695 | 5.2 | MPsi | |
| 彈性系數(shù) | +23℃ | ASTM D638 | 3100 | MPa | |
| 彎曲降服強(qiáng) | +73℉ | ASTM D790 | 14.3 | MPsi | |
| lzod沖擊強(qiáng)度 | 40℃ | ASTM D256 | 96.1 | j/m | |
| 撓曲系數(shù) | +73℉ | 在25℃下 | 380 | MPsi | |
| 伸張強(qiáng)度 | +100℃ | ASTM D638 | 35.9 | MPa | |
| 壓縮應(yīng)力 | +23℃@10%Def. | ASTM D695 | 124 | MPa | |
| 彈性系數(shù) | +73℉ | ASTM D638 | 450 | MPsi | |
| 斷裂時之拉力伸張度 | -68℉(-55℃) | ASTM D638 | 38 | % | |
| 無切口沖擊程度 | +73℉ | ASTM D256 | >100(no break) | ft.lb/in | |
| 壓縮應(yīng)力 | +23℃@1%Def. | ASTM D695 | 35.9 | MPa | |
| 斷裂時之拉力伸張度 | +212℉(+100℃) | ASTM D638 | >260 | % | |
| lzod沖擊強(qiáng)度 | -40℉ | ASTM D256 | 1.8 | ft.lb/in | |
| 伸張強(qiáng)度 | +23℃ | ASTM D-638 | 68.9 | MPa | |
| 負(fù)載下之變形 | 2000psi@+122℉(14Mpa@50℃ | ASTM D621 | 0.5 | % | |
| 伸張強(qiáng)度 | -68℉ | ASTM D638 | 14.7 | MPsi | |
| 撓曲系數(shù) | +23℃ | 在25℃下 | 2620 | MPa | |
| 伸張強(qiáng)度 | +158℉(+70℃) | ASTM D638 | 6.9 | MPsi | |
| 伸張強(qiáng)度 | +70℃ | ASTM D638 | 47.5 | MPa | |
| 彎曲疲勞忍耐限度 | +73℉ | ASTM D671 | 4.7 | MPsi | |
| 伸張強(qiáng)度 | +73℉ | ASTM D638 | 10.0 | MPsi | |
| 壓縮應(yīng)力 | +73°F@10%Def. | ASTM D695 | 18.0 | MPsi | |
| 剪力 | +73℉ | ASTM D732 | 9.5 | MPsi | |
| 撓曲系數(shù) | +100℃ | 在25℃下 | 895 | MPa | |
| 剪力 | +23℃ | ASTM D732 | 65.5 | MPa | |
| 拉力沖擊抵抗力 | +73℉ | D1822Long | 170 | ft.lb/in2; | |
| 斷裂時之拉力伸張度 | +73℉(+23℃) | ASTM D638 | 75 | % | |
| 伸張強(qiáng)度 | +250℉ | ASTM D638 | 3.8 | MPsi | |
| lzod沖擊強(qiáng)度 | +73℉ | ASTM D256 | 2.3 | ft.lb/in | |
| 拉力沖擊抵抗 | +23℃ | D1822Long | 350 | KJ/m2 | |
| 彎曲疲勞忍耐限度 | +23℃ | ASTM D671 | 32.4 | MPa | |
| 撓曲系數(shù) | +158℉ | 在25℃下 | 225 | MPsi | |
| 斷裂時之拉力伸張度 | +250℉(+122℃ | ASTM D638 | >260 | % | |
| 電氣性能 | 電弧抵抗力 | 120mil(3.1mm) | ASTM D495 | 220no tracking | Sec. |
| 熱性能 | 熔點(diǎn) | ASTM D2133 | 347 | °F | |
| 熱變形溫度 | 1.8MPa | ASTM D648 | 136 | ℃ | |
| 線性熱膨脹系數(shù) | +85 to +140℉ | ASTM D696 | 6.8 | 10-5in/in.℉ | |
| 線性熱膨脹系數(shù) | +140 to +220℉ | ASTM D696 | 7.6 | 10-5in/in.℉ | |
| 線性熱膨脹系數(shù) | -40 to +85℉ | ASTM D696 | 5.8 | 10-5in/in.℉ | |
| 線性熱膨脹系數(shù) | -40 to +29℃ | ASTM D696 | 10.4 | 10-5m/m.℃ | |
| 熱變形溫度 | 264psi | ASTM D648 | 277 | ℉ | |
| 線性熱膨脹系數(shù) | +60 to +104℃ | ASTM D696 | 13.7 | 10-5m/m.℃ | |
| 熔點(diǎn) | ASTM D2133 | 175 | ℃ | ||
| 熱傳導(dǎo)系數(shù) | 0.37 | W/mk | |||
| 熱變形溫度 | 0.5Mpa | ASTM D648 | 172 | ℃ | |
| 熱傳導(dǎo)系數(shù) | 2.6 | BTU-in/hr | |||
| 線性熱膨脹系數(shù) | +220 to +300℉ | ASTM D696 | 8.3 | 10-5in/in.℉ | |
| 熱變形溫度 | 66psi | ASTM D648 | 342 | ℉ | |
| 線性熱膨脹系數(shù) | +104 to +150℃ | ASTM D696 | 14.9 | 10-5m/m.℃ | |
| 線性熱膨脹系數(shù) | +29 to +60℃ | ASTM D696 | 12.2 | 10-5m/m.℃ | |
| 其它性能 | 可燃燒性 | UL94 | 94HB | ||
POM材料特性 聚甲醛POM-概述：
POM（聚甲醛樹脂）定義：聚甲醛是一種沒有側(cè)鏈、高密度、高結(jié)晶性的線型聚合物,。按其分子鏈中化學(xué)結(jié)構(gòu)的不同，可分為均聚甲醛和共聚甲醛兩種,。兩者的重要區(qū)別是：均聚甲醛密度,、結(jié)晶度,、熔點(diǎn)都高,，但熱穩(wěn)定性差,，加工溫度范圍窄（約10℃），對酸堿穩(wěn)定性略低,；而共聚甲醛密度,、結(jié)晶度、熔點(diǎn),、強(qiáng)度都較低,，但熱穩(wěn)定性好，不易分解,，加工溫度范圍寬（約50℃）,，對酸堿穩(wěn)定性較好。是具有優(yōu)異的綜合性能的工程塑料,。有良好的物理,、機(jī)械和化學(xué)性能，尤其是有優(yōu)異的耐摩擦性能,。俗稱賽鋼或奪鋼,，為第三大通用塑料,。 適于制作減磨耐磨零件,傳動零件,以及化工,儀表等零件,。
POM材料特性 聚甲醛POM-一般性能:
聚甲醛是一種表面光滑、有光澤的硬而致密的材料,，淡黃或白色,，薄壁部分呈半透明,。燃燒特性為容易燃燒，離火后繼續(xù)燃燒,，火焰上端呈黃色,，下端呈藍(lán)色，發(fā)生熔融滴落,，有強(qiáng)烈的刺激性甲醛味,、魚腥臭。聚甲醛為白色粉末,，一般不透明,，著色性好， 比重1.41-1.43克/立方厘米,，成型收縮率1.2-3.0%,，成型溫度170-200℃ ，干燥條件80-90℃ 2小時,。POM的長期耐熱性能不高,，但短期可達(dá)到160℃，其中均聚POM短期耐熱比共聚POM高10℃以上,，但長期耐熱共聚POM反而比均聚POM高10℃左右,。可在-40℃～100℃溫度范圍內(nèi)長期使用,。POM極易分解,，分解溫度為240度。分解時有刺激性和腐蝕性氣體發(fā)生,。故模具鋼材宜選用耐腐蝕性的材料制作,。
POM材料特性 聚甲醛POM-力學(xué)性能：
POM強(qiáng)度、剛度高,，彈性好,，減磨耐磨性好。其力學(xué)性能優(yōu)異,，比強(qiáng)度可達(dá)50.5MPa,，比剛度可達(dá)2650MPa，與金屬十分接近,。POM的力學(xué)性能隨溫度變化小,，共聚POM比均聚POM的變化稍大一點(diǎn)。POM的沖擊強(qiáng)度較高,，但常規(guī)沖擊不及ABS和PC,；POM對缺口敏感，有缺口可使沖擊強(qiáng)度下降90%之多。POM的疲勞強(qiáng)度十分突出,，10交變載荷作用后,，疲勞強(qiáng)度可達(dá)35MPa，而PA和PC僅為28MPa,。POM的蠕變性與PA相似,，在20℃、21MPa,、3000h時僅為2.3%,，而且受溫度的影響很小。POM的摩擦因數(shù)小,，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC）,，極限PV值很大，自潤滑性好,。POM制品對磨時,，高載荷作用時易產(chǎn)生類似尖叫的噪聲。
POM材料特性 聚甲醛POM-改性:
⒈增強(qiáng)POM 主要增強(qiáng)材料為玻璃纖維,、玻璃球或碳纖維等,，并且玻璃纖維最常用，增強(qiáng)后的力學(xué)性能可提高2～3倍,，熱變形溫度提高50℃以上,。⒉高潤滑POM 在POM中加入石墨、F4,、二硫化鉬,、潤滑油及低分子量PE等，可提高其潤滑性能,。例如,，在POM中加入5份F4，可降低摩擦因數(shù)60%,，耐磨性提高1～2倍,。再如，在POM中加入液體潤滑油,，可大幅度提高耐磨性和極限PV值,。為提高由油的分散效果，需加入炭黑,、氫氧化鋁硫酸鋇,、乙丙橡膠等吸油載體。加入5%油POM的摩擦性提高72%,，極限PV值可達(dá)3.9MPa?m/s（純POM為0.213MPa?m/s）,，為其他工程塑料的3～20倍。