產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.955 | g/cm3 | ||
| 熔體流動速率 | MI | 190℃/2.16kg | ASTM D-1238 | 0.35 | g/10min | |
| HLMI | 190℃/21.6kg | ASTM D-1238 | 33 | g/10min | ||
| 機械性能 | 屈服拉伸強度 | 50mm/min | ASTM D-638 | 27 | MPa | |
| 肖氏硬度 | ASTM D-2240 | 63 | ||||
| 正切彎曲模量 | ASTM D-790 | 1370 | MPa | |||
| 斷裂伸長率 | 50mm/min | ASTM D-638 | >600 | % | ||
| 耐環(huán)境應(yīng)力開裂性 | 條件A,F50100% lgepal | ASTM D-1693 | 45 | h | ||
| 耐環(huán)境應(yīng)力開裂性 | 條件B,F50100% lgepal | ASTM D-1693 | 35 | h | ||
| 熱性能 | 脆化溫度 | ASTM D-746 | <-75 | ℃ | ||