產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重 | ASTM D792 | 1.77-1.8 | g/cm3 | |
| 熔體流動(dòng)速率 | 450℃/12.5 kg | ASTM D1238 | 10-20 | g/10 min | |
| 吸水率 | 23℃, 24 hr | ASTM D570 | 0.03-0.05 | % | |
| 機(jī)械性能 | 硬度計(jì)硬度 | 支撐 D, 23℃ | ASTM D2240 | 70-75 | |
| 拉伸模量 | 23℃ | ASTM D638 | 1030-1520 | MPa | |
| 抗張強(qiáng)度 | 屈服, 23℃ | ASTM D638 | 31-41.4 | MPa | |
| 斷裂, 23℃ | ASTM D638 | 27.6-48.3 | MPa | ||
| 伸長(zhǎng)率 | 屈服, 23℃ | ASTM D638 | 5-15 | % | |
| 斷裂, 23℃ | ASTM D638 | 30-200 | % | ||
| 彎曲模量 | 23℃ | ASTM D790 | 1030-1240 | MPa | |
| 彎曲強(qiáng)度 | 5.0% 應(yīng)變,23℃ | ASTM D790 | 20.7-34.5 | MPa | |
| 壓縮強(qiáng)度 | 23℃ | ASTM D695 | 41.4-58.6 | MPa | |
| 摩擦系數(shù) | 與鋼 - 動(dòng)態(tài) | ASTM D1894 | 0.19 | ||
| 與鋼 - 靜態(tài) | ASTM D1894 | 0.26 | |||
| 抗泰伯磨耗 | 1000 Cycles, 1000 g, CS-17 轉(zhuǎn)輪 | 6-9 | mg | ||
| 懸壁梁缺口沖擊強(qiáng)度 | 23℃ | ASTM D256 | 110-430 | J/m | |
| 熱性能 | 熱變形溫度 | 0.45 MPa, 未退火 | ASTM D648 | 60-75 | ℃ |
| 1.8 MPa, 未退火 | ASTM D648 | 37.8-55 | ℃ | ||
| 玻璃轉(zhuǎn)化溫度 | DSC | DMA | -40.6 到 -38.3 | ℃ | |
| 熔融溫度 | ASTM D3418 | 155-160 | ℃ | ||
| 線形膨脹系數(shù) - 流動(dòng) | ASTM D696 | 0.00013-0.00019 | cm/cm/℃ | ||
| 比熱 | DSC | 1170-1510 | J/kg/℃ | ||
| 導(dǎo)熱系數(shù) | ASTM C177 | 0.14-0.18 | W/m/K | ||
| 阻燃等級(jí) | UL 94 | V-0 | |||
| 電氣性能 | 體積電阻率 | 20℃ | ASTM D257 | 2.0E+14 | ohm·cm |
| 介電強(qiáng)度 | 23℃ | ASTM D149 | 51-63 | kV/mm | |
| 介電常數(shù) | 23℃ | ASTM D150 | 3.5-10.2 | ||
| 耗散因數(shù) | 23℃, 100 Hz | ASTM D150 | 0.01-0.22 | ||
| 光學(xué)性能 | 折射率 | ASTM D542 | 1.42 | ||
| 其它 | 極限氧指數(shù) | ASTM D2863 | 75 | % | |
| ASTM D2863 | 43 | % | |||