| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動(dòng)速率 | 220℃×10kgf(98N) | ASTM D-1238(ISO 1133) | 20 | g/10min |
| 熔體流動(dòng)速率 | 200℃×5kgf(49N) | ASTM D-1238(ISO 1133) | 1.8 | g/10min | |
| 物理性能 | 比重 | 23℃/23℃ | ASTM D-792(ISO 1183) | 1.05 | |
| 機(jī)械性能 | 洛氏硬度 | 23℃ | ASTM D-785(ISO 2039/2) | R-110 | R Scale |
| IZOD沖擊強(qiáng)度 | 23℃,1/4"厚 | ASTM D-256(ISO R180) | 14(137) | kg.cm/cm(J/m) | |
| 彎曲模數(shù) | 23℃ | ASTM D-790(ISO 178) | 28000(2750) | kg/cm2(MPa) | |
| 抗張強(qiáng)度 | 23℃ | ASTM D-638(ISO 527) | 530(52) | kg/cm2(MPa) | |
| 彎曲強(qiáng)度 | 23℃ | ASTM D-790 | 870(86) | kg/cm2(MPa) | |
| 熱性能 | 衛(wèi)氏軟化點(diǎn) | 1kg load | ASTM D-1525(ISO 306) | 103 | ℃ |
| 熱變形溫度 | Unannealed 18.6kg/cm2(1/2"厚) | ASTM D-648(ISO 75/A) | 88 | ℃ | |
| 燃燒性 | UL 94 | 1/16"HB ALL Color | |||
| 熱變形溫度 | Annealed(80℃×8hr) | ASTM D-648(ISO 75/A) | 100 | ℃ | |