產(chǎn)品參數(shù)
產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 性能 | 吸水量 | 50%相對(duì)濕度 | ASTM D-570 | 0.21 | % |
| 吸水量 | 24小時(shí)浸漬 | ASTM D-570 | 0.23 | % | |
| 吸水量 | 浸漬平衡點(diǎn) | ASTM D-570 | 0.90 | % | |
| 比重 | ASTM D-792 | 1.41 | |||
| 自燃性 | UL 94 | HB | |||
| IZOD沖擊試驗(yàn) | 無(wú)缺口23℃ | ASTM D-256 | >5300 | j/m | |
| 破裂點(diǎn)拉伸變形量 | 100℃ | ASTM D-638 | >260 | % | |
| 洛氏硬度 | ASTM D-785 | 94 | M scale | ||
| 撓曲系數(shù) | 70℃ | ASTM D-790 | 1580 | MPa | |
| 線性熱膨脹系數(shù) | 104～160℃ | ASTM D-696 | 14.0 | 10-5m/m℃ | |
| 破裂點(diǎn)拉伸變形量 | -55℃ | ASTM D-638 | 40 | % | |
| 撓曲變形強(qiáng)度 | 23℃ | ASTM D-790 | 98 | MPa | |
| 熔點(diǎn) | ASTM D-2133 | 175 | ℃ | ||
| 熱畸變溫度 | 1.8MPa | ASTM D-648 | 136 | ℃ | |
| 熱畸變溫度 | 0.5MPa | ASTM D-648 | 172 | ℃ | |
| 撓曲系數(shù) | 122℃ | ASTM D-790 | 685 | MPa | |
| 抗剪強(qiáng)度 | 23℃ | ASTM D-732 | 66 | MPa | |
| IZOD沖擊試驗(yàn) | 23℃ | ASTM D-256 | 135 | j/m | |
| 拉伸強(qiáng)度 | 70℃ | ASTM D-638 | 45 | MPa | |
| 壓縮應(yīng)力 | 23℃,10%變形 | ASTM D-695 | 123 | MPa | |
| 破裂點(diǎn)拉伸變形量 | 23℃ | ASTM D-638 | 65 | % | |
| 抗電弧 | 3.1mm | ASTM D-495 | 220 | sec | |
| 彈性系數(shù) | 23℃ | ASTM D-638 | 3220 | MPa | |
| IZOD沖擊試驗(yàn) | 缺口-40℃ | ASTM D-256 | 95 | j/m | |
| 抗拉伸沖擊強(qiáng)度 | 長(zhǎng)試片23℃ | ASTM D-1822 | 525 | kj/m2 | |
| 模收縮 | ASTM D-2133 | 2.2-2.4 | % | ||
| 拉伸強(qiáng)度 | 122℃ | ASTM D-638 | 26 | MPa | |
| 介電強(qiáng)度 | 瞬間Short time(2.3mm) | ASTM D-149 | 19.7 | kv/mm | |